The fracture morphologies of single PA fibers are examined by scanning electron microscopyThe analysis reveals that fiber cutting can be distinguished according to four distinct stages of fiber failure represented by shearing, cutting, brittle fracture, and tensile failure, which are the result of different mechanisms active during the processes

The fracture morphologies of single PA fibers are examined by scanning electron microscopyThe analysis reveals that fiber cutting can be distinguished according to four distinct stages of fiber failure represented by shearing, cutting, brittle fracture, and tensile failure, which are the result of different mechanisms active during the processes of crack initiation, extension and fracture.

The fracture morphologies of single PA fibers are examined by scanning electron microscopyThe analysis reveals that fiber cutting can be distinguished according to four distinct stages of fiber failure represented by shearing, cutting, brittle fracture, and tensile failure, which are the result of different mechanisms active during the processes of crack initiation, extension, and fracture.

fracture failure and the mechanisms affecting cutting resistance To facilitate the above stated goals, this paper investigates the fracture mechanics of single PA fibers using a custom designed fiber cutting performance test benchThe fracture

DOI polym Corpus ID Fracture Failure Mechanisms of Long Single PA Fibers @article{DingFractureFM, title={Fracture Failure Mechanisms of Long Single PA Fibers}, author={HDing and YZhang and Zhitao He}, journal

The present study investigates the failure mechanisms of industrial fiber materials, using a custom designed fiber cutting performance test benchThe fracture morphologies of single PA fibers

The present study investigated the failure mechanisms of long single PA fibers using a custom designed fiber cutting performance test benchThe fracture morphologies were examined by SEMThe analysis revealed that the fiber cutting process can be distinguished according to an initial stage, compression stage, and a fiber failure stage.

Fracture Failure Mechanisms of Long Single PA Fibers Huiling Ding ,, Yongzhen Zhang , and Zhitao He School of Mechanical Engineering, Northwestern Polytechnical University, Xian